In contrast to UO2 and PuO2, there is no consensus on the existence of mixed valence NpO2+x, resulting in a gap between NpO2 and Np2O5 (the highest binary oxide of Np) in the Np-O phase diagram. We now show NpO2+x via Np LIII Extended X-ray Absorption Fine Structure (EXAFS) spectra of three samples of NpO2 that, analogous to U and Pu, exhibit multisite Np-O distributions with varying numbers of oxygen atoms at 1.87–1.91 Å. This is supported by the diffraction pattern of the sample with the largest amount of this oxo-type species that can be refined with both the simple fluorite structure and a trigonal one related to α-U4O9. The implied Np(V)-bridging oxo moieties as well as possible indications of OH¯ found by detailed EXAFS analysis suggest that NpO2+x more closely resembles PuO2+x than UO2+x. An additional common characteristic suggested by the EXAFS and X-Ray Diffraction (XRD) is the phase separation into NpO2 and what would be previously unreported Np4O9(–δ), indicative of O clustering.

Pyrochlore (A₂B₂O₇) is an important, isometric structure-type because of its large variety of compositions and structural derivatives that are generally related to different disordering mechanisms at various spatial scales. The disordering is key to understanding variations in properties, such as magnetic behavior or ionic conduction. Neutron and X-ray total scattering methods were used to investigate the degree of structural disorder in the Ho₂Ti_2-x Zr _x O₇ (x = 0.0-2.0, Δx = 0.25) solid solution series as a function of the Zr-content, x. Ordered pyrochlores (Fd3̄m) disorder to defect fluorite (Fm3̄m) via cation and anion disordering. Total scattering experiments with sensitivity to the cation and anion sublattices provide unique insight into the underlying atomic processes. Using simultaneous Rietveld refinement (long-range structure) and small-box refinement PDF analysis (short-range structure), we show that the series undergoes a rapid transformation from pyrochlore to defect fluorite at x ≈ 1.2, while the short-range structure exhibits a linear increase in a local weberite-type phase, C222₁, over the entire composition range. Enthalpies of formation from the oxides determined using high temperature oxide melt solution calorimetry support the structural data and provide insight into the effect of local ordering on the energetics of disorder. The measured enthalpies of mixing are negative and are fit by a regular solution parameter of W = -31.8 ± 3.7 kJ mol^-1. However, the extensive short-range ordering determined from the structural analysis strongly suggests that the entropies of mixing must be far less positive than implied by the random mixing of a regular solution. We propose a local disordering scheme involving the pyrochlore 48f to 8a site oxygen Frenkel defect that creates 7-coordinated Zr sites contained within local weberite-type coherent nanodomains. Thus, the solid solution is best described as a mixture of two phases, with the weberite-type nanodomains triggering the long-range structural transformation to defect fluorite after accumulation above a critical concentration (50% Ti replaced by Zr).