A rationalized interfacial design strategy was applied to tailor the porous transport layer (PTL)-catalyst layer (CL) contact and the PTL bulk-phase architecture. Particularly, at the PTL-CL interface, our results reveal that laser ablated sintered titanium power-based PTLs improve electrolyzer performance at both the H2NEW Consortium baseline catalyst loading of 0.4 mgIr·cm−2 as well as at the ultra-low catalyst loading of 0.055 mgIr·cm−2. Under ultra-low catalyst loadings, the laser ablated PTL demonstrates maximum reduction of 230 mV compared to the commercial PTL at 4 A·cm−2, and reduces by 68 mV at 3.2 A·cm−2 under H2NEW baseline loading. Laser ablation alters the titanium phase at the interface, so it forms more uniform structure like a microporous layer or a backing layer, leading to an increase in the surface area in contact with the catalyst layer while preventing the membrane from deforming into the PTL. Moreover, we reveal that bulk-phase architecture modification of the PTL by ablating patterned pores at the flow field-PTL interface improves mass transport without sacrificing contact at the CL-PTL interface. Overall, laser ablation of the PTL is an effective method to customize interfacial design to enhance proton exchange membrane electrolyzer performance.

Reactive impinging flow (RIF) is a novel quality-control method for defect detection (i.e., reduction in Pt catalyst loading) in gas-diffusion electrodes (GDEs) on weblines. The technique uses infrared thermography to detect temperature of a nonflammable (<4% H2) reactive mixture of H2/O2 in N2 impinging and reacting on a Pt catalytic surface. In this paper, different GDE size defects (with catalyst-loading reductions of 25, 50, and 100%) are detected at various webline speeds (3.048 and 9.144 m min−1) and gas flowrates (32.5 or 50 standard L min−1). Furthermore, a model is developed and validated for the technique, and it is subsequently used to optimize operating conditions and explore the applicability of the technique to a range of defects. The model suggests that increased detection can be achieved by recting more of the impinging H2, which can be accomplished by placing blocking substrates on the top, bottom, or both of the GDE; placing a substrate on both results in a factor of four increase in the temperature differential, which is needed for smaller defect detection. Overall, the RIF technique is shown to be a promising route for in-line, high-speed, large-area detection of GDE defects on moving weblines.

Water electrolyzers can transform intermittent renewable energy like solar energy and wind energy into the chemical energy of hydrogen with zero greenhouse-gas emissions. The hydroxide-exchange membrane electrolyzer (HEME) combines the capability to produce pressurized hydrogen with the advantage of being able to use low or non-platinum group metal (PGM) electrocatalysts in the alkaline environment.1 Hydroxide salts, for example, KOH, are added to the HEME water feed on both anode and cathode to improve its performance. However, the specific mechanism of performance improvement still needs to be further understood. In addition, at high current densities, bubble evolution can result in mass-transport limitations, a less well studied phenomena. Mathematical modeling is ideal to explore these issues as it is cost and time efficient and can deconvolute the physics, processes, and observed phenomena and study the applied-voltage breakdown. In this work, we extend our previously developed 1D two-phase continuum model2 to study the varies processes in the HEME and provide insights on performance optimizations. First, the oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) kinetics at different hydroxide concentrations have been studied by rotating disk electrodes (RDE) and implemented in the model. Then, the model is calibrated and validated against experimental HEME polarization curves for different KOH concentrations as a liquid electrolyte. The model clearly shows a performance increase with increasing KOH concentrations, which is consistent with the experimental results. The reduced ohmic resistance and increased electrochemical active surface area (ECSA) are the two main reasons for performance increase. The large amount of hydroxide in the liquid electrolyte not only helps to distribute the reactant hydroxide throughout the catalyst layer (CL), which reduces ohmic loss, but also enables reaction at the interface between the liquid electrolyte and electrocatalyst, which increases the ECSA. Applied-voltage breakdown demonstrates that the electrolyzer performance is dominated by anode kinetics and ohmic loss. A comparison with the DI water feed shows a more uniform current distribution in the anode CL when KOH is added, which indicates a higher utilization of the CL. Second, we present modeling on the effects of bubble coverage. As gas evolves, part of the ECSA is minimized due to bubble coverage. To account for this effect, an empirical relationship between the fractional bubble coverage and the current density is implemented in the model.3 The model shows this bubble coverage effect is more pronounced at large current densities with DI water feed. Acknowledgements This work was funded under the HydroGEN Consortium by the Energy Efficiency and Renewable Energy, Hydrogen and Fuel Cell Technologies Office, of the U. S. Department of Energy under contract number DE-AC02-05CH11231. References R. Abbasi, B. P. Setzler, S. Lin, J. Wang, Y. Zhao, H. Xu, B. Pivovar, B. Tian, X. Chen, G. Wu and Y. Yan, 31, 1805876 (2019). L. N. Stanislaw, M. R. Gerhardt and A. Z. Weber, ECS Transactions, 92, 767 (2019). H. Vogt and R. J. Balzer, Electrochimica Acta, 50, 2073 (2005).

Anion exchange membrane fuel cells may enable future operation with non-precious metal-based catalysts. These systems have a delicate sensitivity to operating conditions such as humidification levels and the presence of CO2 in the air oxidant stream. We present spatially resolved in-situ performance results that shed light on phenomena that are unique to anion exchange membrane fuel cells. For cell construction, a highly conductive perfluorinated anion exchange polymer was used as the membrane and the material in powder form as the ionomer. Experiments were conducted to investigate the effects of humidification, fuel/oxidant concentration, and carbonation effects on the performance and its distribution in the cell. The results indicated that (i) dry conditions at the cathode have a stronger effect than at the anode on overall cell performance, (ii) performance significantly suffered when humidification was below 90%, (iii) fuel and oxidant dilution effects lead mass-transport losses and were stronger than flow rate effects, (iv) CO2 in the cathode feed stream creates an equilibration disparity between the inlet and outlet sections and CO2 purging is affected by flooding conditions, and (v) after >500 h of operation, performance deteriorates predominantly at the inlet.

Many solid-state devices, especially those requiring anion conduction, often add a supporting electrolyte to enable efficient operation. The prototypical case is that of anion-exchange-membrane water electrolyzers (AEMWEs), where addition of an alkali metal solution improves performance. However, the specific mechanism of this performance improvement is currently unknown. This work investigates the functionality of the alkali metal solution in AEMWEs using experiments and mathematical models. The results show that additional hydroxide plays a key role not only in ohmic resistance of the membrane and catalyst layer but also in the reaction kinetics. The modeling suggests that the added liquid electrolyte creates an additional electrochemical interface with the electrocatalyst that provides ion-transport pathways and distributes product gas bubbles; the total effective electrochemical active surface area in the cell with 1 M KOH is 5 times higher than that of the cell with DI water. In the cell with 1 M KOH, more than 80% of the reaction current is associate with the liquid electrolyte. These results indicate the importance of high pH of electrolyte and catalyst/electrolyte interface in AEMWEs. The understanding of the functionality of the alkali metal solution presented in this study should help guide the design and optimization of AEMWEs.