Objective

Improved methods are needed to remineralize dentin caries in order to promote conservation of dentin tissue and minimize the surgical interventions that are currently required for clinical treatment. Here, we test the hypothesis that bulk substrates can be effectively mineralized via a dual analog system proposed by others, using a tripolyphosphate (TPP) "templating analog" and a poly(acrylic acid) (PAA) or poly(aspartic acid) (pAsp) "sequestration analog," the latter of which generates the polymer-induced liquid-precursor (PILP) mineralization process studied in our laboratory.

Material & methods

Demineralized human dentin slices were remineralized with and without pre-treatment with TPP, using either PAA or pAsp as the PILP process-directing agent. A control experiment with no polymer present was used for comparison.

Results

No mineralization was observed in any of the PAA groups. In both the pAsp and no polymer groups, TPP inhibited mineralization on the surfaces of the specimens but promoted mineralization within the interiors. Pre-treatment with TPP enhanced overall mineralization of the pAsp group. However, when analysed via TEM, regions with little mineral were still present.

Conclusion

Poly(acrylic acid) was unable to remineralize demineralized dentin slices under the conditions employed, even when pre-treated with TPP. However, pre-treatment with TPP enhanced overall mineralization of specimens that were PILP-remineralized using pAsp.

Objective

Improved methods are needed to remineralize dentin caries in order to promote conservation of dentin tissue and minimize the surgical interventions that are currently required for clinical treatment. Here, we test the hypothesis that bulk substrates can be effectively mineralized via a dual analog system proposed by others, using a tripolyphosphate (TPP) "templating analog" and a poly(acrylic acid) (PAA) or poly(aspartic acid) (pAsp) "sequestration analog," the latter of which generates the polymer-induced liquid-precursor (PILP) mineralization process studied in our laboratory.

Material & methods

Demineralized human dentin slices were remineralized with and without pre-treatment with TPP, using either PAA or pAsp as the PILP process-directing agent. A control experiment with no polymer present was used for comparison.

Results

No mineralization was observed in any of the PAA groups. In both the pAsp and no polymer groups, TPP inhibited mineralization on the surfaces of the specimens but promoted mineralization within the interiors. Pre-treatment with TPP enhanced overall mineralization of the pAsp group. However, when analysed via TEM, regions with little mineral were still present.

Conclusion

Poly(acrylic acid) was unable to remineralize demineralized dentin slices under the conditions employed, even when pre-treated with TPP. However, pre-treatment with TPP enhanced overall mineralization of specimens that were PILP-remineralized using pAsp.

Objective

The polymer-induced liquid-precursor (PILP) mineralization process has been shown to remineralize artificial dentin lesions to levels consistent with those of native dentin. However, nanoindentation revealed that the moduli of those remineralized lesions were only ∼50% that of native dentin. We hypothesize that this may be due to the PILP process having been previously optimized to obtain high amounts (∼70wt%) of intrafibrillar crystals, but without sufficient interfibrillar mineral, another significant component of dentin.

Methods

Fluoride was added to the PILP-mineralization of collagen from rat tail tendon at varying concentrations to determine if a better balance of intra- versus inter-fibrillar mineralization could be obtained, as determined by electron microscopy. Nanoindentation was used to determine if fluoridated apatite could improve the mechanical properties of the composites.

Results

Fluoride was successfully incorporated into the PILP-mineralization of rat tail tendon and resulted in collagen-mineral composite systems with the mineral phase of hydroxyapatite containing various levels of fluoridation. As the fluoride concentration increased, the crystals became larger and more rod-like, with an increasing tendency to form on the fibril surfaces rather than the interior. Nanomechanical testing of the mineralized tendons revealed that fluoride addition did not increase modulus over PILP mineralization alone. This likely resulted from the separated nature of collagen fibrils that comprise tendon, which does not provide lateral reinforcement and therefore may not be suited for the compressive loads of nanoindentation.

Significance

This work contributes to the development of minimally invasive approaches to caries treatment by determining if collagen can be functionally mineralized.

The aim of this study was to evaluate the feasibility of applying the polymer-induced liquid-precursor (PILP) method to enhance silver diamine fluoride (SDF) therapy. One hundred forty micrometer deep artificial caries lesions were treated with (A) 38% SDF solution and (B) 38% SDF containing poly-L-aspartic acid (pASP). Changes in the nanomechanical profile across the lesion were evaluated. Hydrated artificial lesions had a low reduced elastic modulus (0.3 GPa) and nanohardness (0.02 GPa) region extending about 100 μm into the lesion, with a gradual linear increase to about 168 μm where the values plateaued to around 18 GPa/1.0 GPa. Topical application of SDF resulted in significantly recovered properties (p<0.001). SDF containing pASP resulted in greater nanomechanical properties compared to SDF alone, showing similar sloped regions up to 96 μm, then SDF alone dropped while SDF containing pASP continued at a modest slope until reaching normal at 144 μm. This nanoindentation study shows enhanced SDF therapy using the PILP method.

It was hypothesized that applying the polymer-induced liquid-precursor (PILP) system to artificial lesions would result in time-dependent functional remineralization of carious dentin lesions that restores the mechanical properties of demineralized dentin matrix. 140 µm deep artificial caries lesions were remineralized via the PILP process for 7-28 days at 37°C to determine temporal remineralization characteristics. Poly-L-aspartic acid (27 KDa) was used as the polymeric process-directing agent and was added to the remineralization solution at a calcium-to-phosphate ratio of 2.14 (mol/mol). Nanomechanical properties of hydrated artificial lesions had a low reduced elastic modulus (E(R) = 0.2 GPa) region extending about 70 μm into the lesion, with a sloped region to about 140 μm where values reached normal dentin (18-20 GPa). After 7 days specimens recovered mechanical properties in the sloped region by 51% compared to the artificial lesion. Between 7-14 days, recovery of the outer portion of the lesion continued to a level of about 10 GPa with 74% improvement. 28 days of PILP mineralization resulted in 91% improvement of E(R) compared to the artificial lesion. These differences were statistically significant as determined from change-point diagrams. Mineral profiles determined by micro x-ray computed tomography were shallower than those determined by nanoindentation, and showed similar changes over time, but full mineral recovery occurred after 14 days in both the outer and sloped portions of the lesion. Scanning electron microscopy and energy dispersive x-ray analysis showed similar morphologies that were distinct from normal dentin with a clear line of demarcation between the outer and sloped portions of the lesion. Transmission electron microscopy and selected area electron diffraction showed that the starting lesions contained some residual mineral in the outer portions, which exhibited poor crystallinity. During remineralization, intrafibrillar mineral increased and crystallinity improved with intrafibrillar mineral exhibiting the orientation found in normal dentin or bone.