This study aims to develop high-capacity hard carbon anode materials for alkali-ion batteries by controlling the microstructures of non-graphitic hard carbon through an annealing protocol and investigating the effects on the alkali-ion storage mechanisms using physical, chemical, and electrochemical analytical techniques. The hard carbon materials were synthesized at temperatures ranging from 900 °C to 1600 °C. Those synthesized at 1100 °C with high surface area and abundant defects exhibited the highest reversible capacity in Li- and K-ion systems, with the storage dominated by surface-adsorption mechanisms. In contrast, the hard carbon compounds prepared at 1400 °C with numerous curve-featured pores delivered the highest reversible capacity in the Na-ion system, indicating that these pores are the preferred Na-ion storage sites, particularly in low-voltage plateau regions. This study provides a comprehensive understanding of the relationship between microstructures and alkali-ion storage mechanisms in non-graphitic hard carbon and highlights the importance of tailoring the microstructures of hard carbon to achieve high specific capacity for the desired alkali-ion species.

This work focuses on the mechanisms of interfacial processes at the surface of amorphous silicon thin-film electrodes in organic carbonate electrolytes to unveil the origins of the inherent nonpassivating behavior of silicon anodes in Li-ion batteries. Attenuated total reflection Fourier-transform infrared spectroscopy, X-ray absorption spectroscopy, and infrared near-field scanning optical microscopy were used to investigate the formation, evolution, and chemical composition of the surface layer formed on Si upon cycling. We found that the chemical composition and thickness of the solid/electrolyte interphase (SEI) layer continuously change during the charging/discharging cycles. This SEI layer "breathing" effect is directly related to the formation of lithium ethylene dicarbonate (LiEDC) and LiPF₆ salt decomposition products during silicon lithiation and their subsequent disappearance upon delithiation. The detected appearance and disappearance of LiEDC and LiPF₆ decomposition compounds in the SEI layer are directly linked with the observed interfacial instability and poor passivating behavior of the silicon anode.