Single-crystal Ni-based superalloys are currently the material of choice for turbine blade applications, especially with the emerging additive manufacturing (AM) that facilitates the manufacture/repair of these single crystals. This promising AM route, however, comes with a dilemma: in the fusion and heat affected zones after e-beam or laser induced melting, one needs a solutionizing annealing to relieve the residual stresses and homogenize the chemical/microstructure. The super-solvus solutionizing temperature is usually adopted from the protocol for the cast superalloys, which almost always causes recrystallization and stray grain growth, resulting in a polycrystalline microstructure and degrading the high-temperature mechanical performance. Here we demonstrate a custom-designed post-printing heat treatment to replace the conventional super-solvus one. The recovery and relatively low temperature diminish the driving force for recrystallization and the movement of stray grain boundaries, without suffocating the chemical/microstructural homogenization thanks to the narrow dendrite width and short element segregation distance. The optimal duration of the heat treatment is proposed to achieve atomic-diffusion mediated chemical homogenization while limiting γ′-particle coarsening in the interdendritic regions. Our strategy makes it practically feasible to resolve several bottleneck problems with one processing/treatment, removing a seemingly formidable obstacle to effective additive manufacturing of superalloy single crystal products.

Laser shock peening (LSP), a surface modification technique, is promising to enhance the strength and wear resistance for Ni-based superalloys. To understand the strengthening mechanism in a laser shock peened Ni-based superalloy DZ417G, we utilize synchrotron poly- and monochromatic X-ray microdiffraction, as well as electron microscopy and microhardness to quantify the local microstructures and mechanical properties at various depths. In the 1.2-mm-deep hardened layer, the microhardness increases monotonically by ∼50% from the unaffected interior to the surface. Quantitative microdiffraction analysis shows that large amounts of dislocations are introduced by LSP. High densities of 7.1 × 1015 m−2 and 11.8 × 1015 m−2 are seen close to the peened surface for the γ- and γ′-phases, respectively, which are 5 and 20 times of those in the unaffected region. Different gradients of dislocation density are observed for the two phases from interior to surface, and their combined effect accounts well for the hardness increment. Due to the unaltered γ′-precipitates and chemical composition in the LSP affected zone, the large density of dislocations dominates the observed strengthening. Combined poly- and monochromatic X-ray microdiffraction allows quantifying the local microstructures of plastic deformation over a large sampling scale that can hardly be achieved using other materials characterization techniques.