Solid oxide electrolysis cell stacks are expected to experience dynamic conditions when using renewable electricity derived from wind or solar power. To address this scenario, (Mn,Co)3O4 (MCO)-coated Crofer 22 APU interconnect coupons are subjected to thermal cycling, and intermittent current density, with gas compositions relevant to high-temperature electrolysis (elevated steam:hydrogen ratio and oxygen content). Defects are also intentionally introduced in the MCO coating, to assess whether the difference in oxidation properties of the adjacent coated and uncoated (defective) surfaces causes sufficient stress to damage the protective oxide scale. Specimens with defects are subjected to oxidation for 1000 h at 800 °C, or thermal cycling. Before thermal cycling, some specimens are pre-oxidized to create a thick oxide scale to mimic the scale thickness expected after ∼30 kh operation. In all cases, the coating and oxide scale remain well adhered with no cracking observed. Area-specific resistance (ASR) is monitored in both single-atmosphere and dual-atmosphere conditions, and the ASR is stable and is not impacted by dynamic cycling of the current density. This work provides confidence that the MCO coated interconnect will function as needed in dynamic operation conditions, even with coating defects.

Mixed transition-metal oxide coatings are commonly applied to stainless steel interconnects for solid oxide cell stacks. Such coatings reduce oxidation and Cr evaporation rates, leading to improved degradation rate and stack lifetime. Here, the ChromLok™ MCO-based composition (Mn,Co)3O4 is applied to Crofer 22 APU stainless steel and evaluated specifically for application in solid oxide electrolyzer stacks operating around 800 °C and utilizing oxygen-ion-conducting solid oxide cells. The MCO coating is found to decrease the stainless steel oxidation rate by about one order of magnitude, and decrease the Cr evaporation rate by fourfold. The coating also dramatically lowers the rate of area-specific resistance increase for stainless steel coupons oxidized for 500 h with constant current applied, from 33 mΩ∗cm2 kh−1 for an uncoated coupon to less than 4 mΩ∗cm2 kh−1 for coated coupons. The coating is demonstrated on full-scale interconnects for single-cells, where the coating dramatically reduces degradation rate, and for a stack, which displays stable operation for 700 h.