Here, we demonstrate that graphite can serve as a versatile electrode for various rechargeable battery types by reversibly accommodating solvated alkali ions (such as K, Na, and Li) through co-intercalation in its galleries. The co-intercalation of alkali ions is observed to occur via staging reactions. Notably, their insertion behaviors, including their specific capacity, are remarkably similar regardless of the alkali ion species despite the different solubility limits of K, Na, and Li ions in graphite. Nevertheless, the insertion potentials of the solvated alkali ions differ from each other and are observed to be correlated with the interlayer distance in the intercalated graphite gallery.

Grid-scale energy storage systems (ESSs) that can connect to sustainable energy resources have received great attention in an effort to satisfy ever-growing energy demands. Although recent advances in Li-ion battery (LIB) technology have increased the energy density to a level applicable to grid-scale ESSs, the high cost of Li and transition metals have led to a search for lower-cost battery system alternatives. Based on the abundance and accessibility of Na and its similar electrochemistry to the well-established LIB technology, Na-ion batteries (NIBs) have attracted significant attention as an ideal candidate for grid-scale ESSs. Since research on NIB chemistry resurged in 2010, various positive and negative electrode materials have been synthesized and evaluated for NIBs. Nonetheless, studies on NIB chemistry are still in their infancy compared with LIB technology, and further improvements are required in terms of energy, power density, and electrochemical stability for commercialization. Most recent progress on electrode materials for NIBs, including the discovery of new electrode materials and their Na storage mechanisms, is briefly reviewed. In addition, efforts to enhance the electrochemical properties of NIB electrode materials as well as the challenges and perspectives involving these materials are discussed.

The intercalation of lithium ions into graphite electrode is the key underlying mechanism of modern lithium-ion batteries. However, co-intercalation of lithium-ions and solvent into graphite is considered undesirable because it can trigger the exfoliation of graphene layers and destroy the graphite crystal, resulting in poor cycle life. Here, it is demonstrated that the [lithium–solvent]+ intercalation does not necessarily cause exfoliation of the graphite electrode and can be remarkably reversible with appropriate solvent selection. First-principles calculations suggest that the chemical compatibility of the graphite host and [lithium–solvent]+ complex ion strongly affects the reversibility of the co-intercalation, and comparative experiments confirm this phenomenon. Moreover, it is revealed that [lithium–ether]+ co-intercalation of natural graphite electrode enables much higher power capability than normal lithium intercalation, without the risk of lithium metal plating, with retention of ≈87% of the theoretical capacity at current density of 1 A g−1. This unusual high rate capability of the co-intercalation is attributed to the (i) absence of the desolvation step, (ii) negligible formation of the solid–electrolyte interphase on graphite surface, and (iii) fast charge-transfer kinetics. This work constitutes the first step toward the utilization of fast and reversible [lithium–solvent]+ complex ion intercalation chemistry in graphite for rechargeable battery technology.

Conversion reaction electrodes offer a high specific capacity in rechargeable batteries by utilizing wider valence states of transition metals than conventional intercalation-based electrodes and have thus been intensively studied in recent years as potential electrode materials for high-energy-density rechargeable batteries. However, several issues related to conversion reactions remain poorly understood, including the polarization or hysteresis during charge/discharge processes. Herein, Co3O4 in Na cells is taken as an example to understand the aforementioned properties. The large hysteresis in charge/discharge profiles is revealed to be due to different electrochemical reaction paths associated with respective charge and discharge processes, which is attributed to the mobility gap among inter-diffusing species in a metal oxide compound during de/sodiation. Furthermore, a Co3O4–graphene nanoplatelet hybrid material is demonstrated to be a promising anode for Na rechargeable batteries, delivering a capacity of 756 mAh g−1 with a good reversibility and an energy density of 96 Wh kg−1 (based on the total electrode weight) when combined with a recently reported Na4Fe3(PO4)2(P2O7) cathode.