Single-crystal Ni-based superalloys are currently the material of choice for turbine blade applications, especially with the emerging additive manufacturing (AM) that facilitates the manufacture/repair of these single crystals. This promising AM route, however, comes with a dilemma: in the fusion and heat affected zones after e-beam or laser induced melting, one needs a solutionizing annealing to relieve the residual stresses and homogenize the chemical/microstructure. The super-solvus solutionizing temperature is usually adopted from the protocol for the cast superalloys, which almost always causes recrystallization and stray grain growth, resulting in a polycrystalline microstructure and degrading the high-temperature mechanical performance. Here we demonstrate a custom-designed post-printing heat treatment to replace the conventional super-solvus one. The recovery and relatively low temperature diminish the driving force for recrystallization and the movement of stray grain boundaries, without suffocating the chemical/microstructural homogenization thanks to the narrow dendrite width and short element segregation distance. The optimal duration of the heat treatment is proposed to achieve atomic-diffusion mediated chemical homogenization while limiting γ′-particle coarsening in the interdendritic regions. Our strategy makes it practically feasible to resolve several bottleneck problems with one processing/treatment, removing a seemingly formidable obstacle to effective additive manufacturing of superalloy single crystal products.

The repair of damaged Ni-based superalloy single-crystal turbine blades has been a long-standing challenge. Additive manufacturing by an electron beam is promising to this end, but there is a formidable obstacle: either the residual stress and γ/γ  ' microstructure in the single-crystalline fusion zone after e-beam melting are unacceptable (e.g., prone to cracking), or, after solutionizing heat treatment, recrystallization occurs, bringing forth new grains that degrade the high-temperature creep properties. Here, a post-3D printing recovery protocol is designed that eliminates the driving force for recrystallization, namely, the stored energy associated with the high retained dislocation density, prior to standard solution treatment and aging. The post-electron-beam-melting, pre-solutionizing recovery via sub-solvus annealing is rendered possible by the rafting (i.e., directional coarsening) of γ  ' particles that facilitates dislocation rearrangement and annihilation. The rafted microstructure is removed in subsequent solution treatment, leaving behind a damage-free and residual-stress-free single crystal with uniform γ  ' precipitates indistinguishable from the rest of the turbine blade. This discovery offers a practical means to keep 3D-printed single crystals from cracking due to unrelieved residual stress, or stress-relieved but recrystallizing into a polycrystalline microstructure, paving the way for additive manufacturing to repair, restore, and reshape any superalloy single-crystal product.