The LiNi0.5Mn1.5O4 spinel is an appealing cathode material for next generation rechargeable Li-ion batteries due to its high operating voltage of ∼4.7 V (vs Li/Li+). Although it is widely believed that the full range of electrochemical cycling involves the redox of Ni(II)/(IV), it has not been experimentally clarified whether Ni(III) exists as the intermediate state or a double-electron transfer takes place. Here, combined with theoretical calculations, we show unambiguous spectroscopic evidence of the Ni(III) state when the LiNi0.5Mn1.5O4 electrode is half charged. This provides a direct verification of single-electron-transfer reactions in LiNi0.5Mn1.5O4 upon cycling, namely, from Ni(II) to Ni(III), then to Ni(IV). Additionally, by virtue of its surface sensitivity, soft X-ray absorption spectroscopy also reveals the electrochemically inactive Ni2+ and Mn2+ phases on the electrode surface. Our work provides the long-awaited clarification of the single-electron transfer mechanism in LiNi0.5Mn1.5O4 electrodes. Furthermore, the experimental results serve as a benchmark for further spectroscopic characterizations of Ni-based battery electrodes.

Recent calculations and experimental data suggest that understanding the local ordering behavior of Ni/Mn will be critical to optimize the electrochemical properties of LiNi0.5Mn1.5O4 (LNMO) high voltage spinel. In this study, we systematically controlled the evolution of Ni and Mn ordering in LNMO samples by annealing them at 700 °C in air for different dwelling times, followed by quenching to room temperature. The long- and short-range ordering behavior of Ni and Mn were analyzed by combining neutron powder diffraction, X-ray powder diffraction (XRD), transmission electron microscopy (TEM), and Fourier transform infrared spectroscopy (FT-IR) data. The results show that the fraction of ordered phase increases rapidly during initial annealing at 700 °C for 6 h, and accompanied by decreasing amounts of secondary phases. Annealing longer than 6 h led to the growth in size of ordered domains (i.e., increased segregation of ordered and disordered domains) along with a slow increase in the fraction of ordered phase. The dependence of open circuit voltages (OCVs) of the LNMO on the degree of ordering agrees well with recent calculations using the density functional theory. The increase in the degree of ordering increases the open circuit voltage (OCV) and the initial capacity but reduces cycle life and rate capability. The LNMO delivered optimal battery performances (capacity, cycle life, and rate capability) after annealing at 700 °C for 2 h. This partially ordered sample showed the respective advantages from both disordered and ordered spinels: better spinel-phase purity (thus, higher initial capacity) from the ordered LNMO and better cycle life and rate capability from the disordered LNMO. © 2014 American Chemical Society.