Although the determination of site occupancies is often a major goal in Rietveld refinement studies, the accurate refinement of site occupancies is exceptionally challenging due to many correlations and systematic errors that have a hidden impact on the final refined occupancy parameters. Through the comparison of results independently obtained from neutron and synchrotron powder diffraction, improved approaches capable of detecting occupancy defects with an exceptional sensitivity of 0.1% (absolute) in the class of layered NMC (Li[Ni_xMn_yCo_z]O₂) Li-ion battery cathode materials have been developed. A new method of visualizing the diffraction parameter space associated with crystallographic site scattering power through the use of f* diagrams is described, and this method is broadly applicable to ternary compounds. The f* diagrams allow the global minimum fit to be easily identified and also permit a robust determination of the number and types of occupancy defects within a structure. Through a comparison of neutron and X-ray diffraction results, a systematic error in the synchrotron results was identified using f* diagrams for a series of NMC compounds. Using neutron diffraction data as a reference, this error was shown to specifically result from problems associated with the neutral oxygen X-ray atomic form factor and could be eliminated by using the ionic O^2- form factor for this anion while retaining the neutral form factors for cationic species. The f* diagram method offers a new opportunity to experimentally assess the quality of atomic form factors through powder diffraction studies on chemically related multi-component compounds.

Lithium-rich NMC (LR-NMC) compounds exhibit high capacities beyond the traditional redox, but it remains unclear whether the anomalous charge compensation mechanism is due to oxidized lattice oxygen or migration-assisted Mn oxidation. We compare LR-NMC with a model Mn7+ system (KMnO4) using a combination of resonant inelastic X-ray scattering (RIXS) irradiation studies and operando X-ray absorption spectroscopy/X-ray diffraction (XAS/XRD) to quantify transition metal (TM) migration, Mn oxidization, and beam-induced effects. We reveal how for KMnO4 it is possible to observe beam-induced Mn reduction resulting in trapped molecular oxygen. For LR-NMC, we observe negligible evidence for Mn oxidation while stabilized tetrahedral sites correlate more with a reduced TM environment. Finally, the additional spectroscopic structures observed in oxidized oxygen RIXS for LR-NMC are absent for gas-phase molecular oxygen.

Sensitivity to the "bulk" oxygen core orbital makes hard X-ray photoelectron spectroscopy (HAXPES) an appealing technique for studying oxygen redox candidates. Various studies have reported an additional O 1s peak (530-531 eV) at high voltages, which has been considered a direct signature of the bulk oxygen redox process. Here, we find the emergence of a 530.4 eV O 1s HAXPES peak for three model cathodes-Li₂MnO₃, Li-rich NMC, and NMC 442-that shows no clear link to oxygen redox. Instead, the 530.4 eV peak for these three systems is attributed to transition metal reduction and electrolyte decomposition in the near-surface region. Claims of oxygen redox relying on photoelectron spectroscopy must explicitly account for the surface sensitivity of this technique and the extent of the cathode degradation layer.

High-nickel content cathode materials offer high energy density. However, the structural and surface instability may cause poor capacity retention and thermal stability of them. To circumvent this problem, nickel concentration-gradient materials have been developed to enhance high-nickel content cathode materials' thermal and cycling stability. Even though promising, the fundamental mechanism of the nickel concentration gradient's stabilization effect remains elusive because it is inseparable from nickel's valence gradient effect. To isolate nickel's valence gradient effect and understand its fundamental stabilization mechanism, we design and synthesize a LiNi_0.8Mn_0.1Co_0.1O₂ material that is compositionally uniform and has a hierarchical valence gradient. The nickel valence gradient material shows superior cycling and thermal stability than the conventional one. The result suggests creating an oxidation state gradient that hides the more capacitive but less stable Ni³⁺ away from the secondary particle surfaces is a viable principle towards the optimization of high-nickel content cathode materials.

State-of-the-art lithium (Li)-ion batteries are approaching their specific energy limits yet are challenged by the ever-increasing demand of today’s energy storage and power applications, especially for electric vehicles. Li metal is considered an ultimate anode material for future high-energy rechargeable batteries when combined with existing or emerging high-capacity cathode materials. However, much current research focuses on the battery materials level, and there have been very few accounts of cell design principles. Here we discuss crucial conditions needed to achieve a specific energy higher than 350 Wh kg −1 , up to 500 Wh kg −1 , for rechargeable Li metal batteries using high-nickel-content lithium nickel manganese cobalt oxides as cathode materials. We also provide an analysis of key factors such as cathode loading, electrolyte amount and Li foil thickness that impact the cell-level cycle life. Furthermore, we identify several important strategies to reduce electrolyte-Li reaction, protect Li surfaces and stabilize anode architectures for long-cycling high-specific-energy cells.