A template-free rapidly mixed reaction was employed to synthesize polyaniline nanofibers using chemical oxidative polymerization of aniline. Hydrochloric acid (HCl) and camphor sulfonic acid (CSA) were used in the synthesis to obtain 30- and 50-nm average diameter polyaniline nanofibers. The nanofibers were deposited onto layered ZnO/64 degrees YX LiNbO3 surface-acoustic-wave transducers. The sensors were tested toward hydrogen (H-2) gas while operating at room temperature. The dopant for the polyaniline nanofiber synthesis was found to have a significant effect on the device sensitivity. The sensor response was found to be larger for the 50-nmdiameter CSA-doped nanofiber based sensors, while the response and recovery times were faster for the 30-nm diameter HCl-doped nanofibers.

A polyaniline/In2O3 nanofibre composite based layered surface acoustic wave ( SAW) sensor has been developed and investigated for different gases. Chemical oxidative polymerization of aniline in the presence of finely divided In2O3 was employed to synthesize a polyaniline nanofibre/In2O3 nanoparticle composite. The nanocomposite was deposited onto a layered ZnO/64 degrees YX LiNbO3 SAW transducer. The novel sensor was exposed to H-2, NO2 and CO gases. Fast response and recovery times with good repeatability were observed at room temperature.