The non-toxic and wide bandgap material TiO2 is explored as an n-type buffer layer on p-type Cu(In,Ga)Se2 (CIGS) absorber layer for thin film solar cells. The amorphous TiO2 thin film deposited by atomic layer deposition process at low temperatures shows conformal coverage on the CIGS absorber layer. Solar cells from non-vacuum deposited CIGS absorbers with TiO2 buffer layer result in a high short-circuit current density of 38.9 mA/cm(2) as compared to 36.9 mA/cm(2) measured in the reference cell with CdS buffer layer, without compromising open-circuit voltage. The significant photocurrent gain, mainly in the UV part of the spectrum, can be attributed to the low parasitic absorption loss in the ultrathin TiO2 layer (~10 nm) with a larger bandgap of 3.4 eV compared to 2.4 eV of the traditionally used CdS. Overall the solar cell conversion efficiency was improved from 9.5% to 9.9% by substituting the CdS by TiO2 on an active cell area of 10.5 mm(2). Optimized TiO2/CIGS solar cells show excellent long-term stability. The results imply that TiO2 is a promising buffer layer material for CIGS solar cells, avoiding the toxic CdS buffer layer with added performance advantage.

In this paper, a post superacid (SA) treatment was proposed to enhance the performance of InAs FinFETs on SiO2/Si substrates. Typically, the subthreshold swing (SS) has reduced from 217 to 170 mV/decade and the transconductance (gm) has increased from 6.44 to 26.5 μS/μm after SA treatment. It was found that the interfacial In2O3 at the InAs/ZrO2 interface was effectively reduced after SA treatment due to the strong protonating nature of the SA solution. As a result, the interface trap density was reduced leading to a pronounced reduction of sheet resistance after SA treatment. The modeling of transfer characteristics indicates that the carrier mobility is enhanced by 5.87.1 folds after SA treatment due to interfacial traps reduction. The results suggest that SA treatment can be potentially extended to other III-V MOSFETs to enhance the device performances.

A flexible and wearable microsensor array is described for simultaneous multiplexed monitoring of heavy metals in human body fluids. Zn, Cd, Pb, Cu, and Hg ions are chosen as target analytes for detection via electrochemical square wave anodic stripping voltammetry (SWASV) on Au and Bi microelectrodes. The oxidation peaks of these metals are calibrated and compensated by incorporating a skin temperature sensor. High selectivity, repeatability, and flexibility of the sensor arrays are presented. Human sweat and urine samples are collected for heavy metal analysis, and measured results from the microsensors are validated through inductively coupled plasma mass spectrometry (ICP-MS). Real-time on-body evaluation of heavy metal (e.g., zinc and copper) levels in sweat of human subjects by cycling is performed to examine the change in concentrations with time. This platform is anticipated to provide insightful information about an individual's health state such as heavy metal exposure and aid the related clinical investigations.

The III-V compound semiconductors exhibit superb electronic and optoelectronic properties. Traditionally, closely lattice-matched epitaxial substrates have been required for the growth of high-quality single-crystal III-V thin films and patterned microstructures. To remove this materials constraint, here we introduce a growth mode that enables direct writing of single-crystalline III-V's on amorphous substrates, thus further expanding their utility for various applications. The process utilizes templated liquid-phase crystal growth that results in user-tunable, patterned micro and nanostructures of single-crystalline III-V's of up to tens of micrometres in lateral dimensions. InP is chosen as a model material system owing to its technological importance. The patterned InP single crystals are configured as high-performance transistors and photodetectors directly on amorphous SiO2 growth substrates, with performance matching state-of-the-art epitaxially grown devices. The work presents an important advance towards universal integration of III-V's on application-specific substrates by direct growth.