Bismuth Selenide (Bi2Se3) is a topological insulator (TI) with a structure consisting of stacked quintuple layers. Single crystal surfaces are commonly prepared by mechanical cleaving. This work explores the use of low energy Ar+ ion bombardment and annealing (IBA) as an alternative method to produce reproducible and stable Bi2Se3 surfaces under ultra-high vacuum (UHV). It is found that a clean and well-ordered surface can be prepared by a single cycle of 1 keV Ar+ ion bombardment and 30 min of annealing. Low energy electron diffraction (LEED) and detailed low energy ion scattering (LEIS) measurements show no differences between IBA-prepared surfaces and those prepared by in situ cleaving in UHV. Analysis of the LEED patterns shows that the optimal annealing temperature is ~450 °C. Angular LEIS scans reveal the formation of surface Se vacancies when the annealing temperature exceeds 520 °C.