UC Berkeley

Calcium silicate hydrate (C-S-H), is the principal hydration product of Portland cement that mainly contributes to the physical and mechanical properties of concrete. This paper aims to investigate the three-dimensional structure of C-S-H with Ca/Si ratios of 1.0 and 1.6 at the nanoscale using electron tomography. The 3D reconstructions and selected region of interest analysis confirm that the morphology of both C-S-H materials are foil-like structures. The difference between the two materials is the density of elongated structures. C-S-H with Ca/Si ratio 1.6 is clearly composed of denser particles compared to the other C-S-H material due to overlapping of the foil-like structure. Pore analysis shows that C-S-H 1.0 and C-S-H 1.6 have porosities 69.2% and 49.8% respectively. Pore size distribution also reveals that C-S-H 1.0 has pore size range between 0-250 nm and C-S-H 1.6 between 0-100 nm. The pore network's size of C-S-H 1.0 is significantly larger than 1.6. This study illustrates the capability of using electron tomography to determine the 3D nanoscale structure of cementitious products and to distinguish between C-S-H 1.0 and 1.6.