The three-dimensional magnetic structure and reversal mechanism of patterned Co/Pt multilayers, were imaged using complementary Lorentz transmission electron microscopy (LTEM) (in-plane component) and magnetic transmission x-ray microscopy (M-TXM) (perpendicular magnetization). The Co/Pt films with perpendicular anisotropy were patterned by ion irradiation through a stencil mask to produce in-plane magnetization in the irradiated regions. The boundaries of the patterns, defined by the transition from out-of-plane to in-plane magnetization, were found to be determined by the stencil mask, whilst the scale of the magnetic reversal by the physical microstructure. The nucleation fields were substantially reduced to 50 Oe for the in-plane regions and 1 kOe for the perpendicular regions, comparing to 4.5 kOe for the as-grown film. The perpendicular reversals were found to always originate at the pattern boundaries.