Thermoelectric materials with high electrical conductivity and low thermal conductivity (e.g., Bi2Te3) can efficiently convert waste heat into electricity; however, in spite of favorable theoretical predictions, individual Bi2Te3 nanostructures tend to perform less efficiently than bulk Bi2Te3. We report a greater-than-order-of-magnitude enhancement in the thermoelectric properties of suspended Bi2Te3 nanoribbons, coated in situ to form a Bi2Te3/F4-TCNQ core-shell nanoribbon without oxidizing the core-shell interface. The shell serves as an oxidation barrier but also directly functions as a strong electron acceptor and p-type carrier donor, switching the majority carriers from a dominant n-type carrier concentration (∼1021 cm-3) to a dominant p-type carrier concentration (∼1020 cm-3). Compared to uncoated Bi2Te3 nanoribbons, our Bi2Te3/F4-TCNQ core-shell nanoribbon demonstrates an effective chemical potential dramatically shifted toward the valence band (by 300-640 meV), robustly increased Seebeck coefficient (∼6× at 250 K), and improved thermoelectric performance (10-20× at 250 K).

Current reports of thermal expansion coefficients (TEC) of two-dimensional (2D) materials show large discrepancies that span orders of magnitude. Determining the TEC of any 2D material remains difficult due to approaches involving indirect measurement of samples that are atomically thin and optically transparent. We demonstrate a methodology to address this discrepancy and directly measure TEC of nominally monolayer epitaxial WSe2 using four-dimensional scanning transmission electron microscopy (4D-STEM). Experimentally, WSe2 from metal-organic chemical vapor deposition (MOCVD) was heated through a temperature range of 18-564 °C using a barrel-style heating sample holder to observe temperature-induced structural changes without additional alterations or destruction of the sample. By combining 4D-STEM measurements with quantitative structural analysis, the thermal expansion coefficient of nominally monolayer polycrystalline epitaxial 2D WSe2 was determined to be (3.5 ± 0.9) × 10-6 K-1 and (5.7 ± 2) × 10-5 K-1 for the in- and out-of-plane TEC, respectively, and (3.6 ± 0.2) × 10-5 K-1 for the unit cell volume TEC, in good agreement with historically determined values for bulk crystals.