Although metal-organic frameworks (MOFs) are being widely used to derive functional nanomaterials through pyrolysis, the actual mechanisms involved remain unclear. In the limited studies to date, elemental metallic species are found to be the initial products, which limits the variety of MOF-derived nanomaterials. Here, the pyrolysis of a manganese triazolate MOF is examined carefully in terms of phase transformation, reaction pathways, and morphology evolution in different conditions. Surprisingly, the formation of metal is not detected when manganese triazolate is pyrolyzed in an oxygen-free environment. Instead, a direct transformation into nanoparticles of manganese nitride, Mn₂N _x embedded in N-doped graphitic carbon took place. The electrically conductive Mn₂N _x nanoparticles show much better air stability than bulk samples and exhibit promising electrocatalytic performance for the oxygen reduction reaction. The findings on pyrolysis mechanisms expand the potential of MOF as a precursor to derive more functional nanomaterials.

The guest-dependent flexibility of the pillared-layered metal-organic framework (MOF), Zn₂bdc₂dabco·X(guest), where guest = EtOH, DMF or benzene, has been examined by high-pressure single crystal X-ray diffraction. A pressure-induced structural phase transition is found for the EtOH- and DMF-included frameworks during compression in a hydrostatic medium of the guest species, which is dependent upon the nature and quantity of the guest in the channels. The EtOH-included material undergoes a phase transition from P4/mmm to C2/m at 0.69 GPa, which is accompanied by a change in the pore shape from square to rhombus via super-filling of the pores. The DMF-included material undergoes a guest-mediated phase transition from I4/mcm to P4/mmm at 0.33 GPa via disordering of the DMF guest. In contrast, the benzene-included framework features a structure with rhombus-shaped channels at ambient pressure and shows direct compression under hydrostatic pressure. These results demonstrate the large influence of guest molecules on the high-pressure phase behavior of flexible MOFs. Guest-mediated framework flexibility is useful for engineering MOFs with bespoke pore shapes and compressibility.