We present a design strategy for fabricating ultrastable phase-pure films of formamidinium lead iodide (FAPbI₃) by lattice templating using specific two-dimensional (2D) perovskites with FA as the cage cation. When a pure FAPbI₃ precursor solution is brought in contact with the 2D perovskite, the black phase forms preferentially at 100°C, much lower than the standard FAPbI₃ annealing temperature of 150°C. X-ray diffraction and optical spectroscopy suggest that the resulting FAPbI₃ film compresses slightly to acquire the (011) interplanar distances of the 2D perovskite seed. The 2D-templated bulk FAPbI₃ films exhibited an efficiency of 24.1% in a p-i-n architecture with 0.5-square centimeter active area and an exceptional durability, retaining 97% of their initial efficiency after 1000 hours under 85°C and maximum power point tracking.