We present a simple, scalable synthesis route for producing exchange coupled soft/hard magnetic composite powder that outperforms pure soft and hard phase constituents.

We present a simple, scalable synthesis route for producing exchange coupled soft/hard magnetic composite powder that outperforms pure soft and hard phase constituents. Importantly, the composites are iron oxide based (SrFe ₁₂ O ₁₉ and Fe ₃ O ₄ ) and contain no rare earth or precious metals. The two step synthesis process consists of first precipitating an iron oxide/hydroxide precursor directly on top of SrFe ₁₂ O ₁₉ nano-flakes, ensuring a very fine degree of mixing between the hard and the soft magnetic phases. The second step involves the reduction of the precursor to create the appropriate soft magnetic phase and create the intimate interface necessary for exchange coupling. We establish a clear processing window; at temperatures below this window the desired soft phase is not produced, while the use of higher temperatures results in deleterious reaction at the soft/hard phase interfaces, causing an improper ratio of soft to hard phases. Improvements in M _r , M _s , and (BH) _max are 42%, 29% and 37%, respectively, in the SrFe ₁₂ O ₁₉ /Fe ₃ O ₄ composite compared to the pure hard phase (SrFe ₁₂ O ₁₉ ). We provide evidence of coupling (exchange spring behavior) with hysteresis curves, first order reversal curve (FORC) analysis and recoil measurements.