Improving the mechanical strength of ceramic solid electrolytes such as lithium phosphorus sulfide families for pressure-driven dendrite blocking as well as reducing the electronic conductivity to prevent a dendrite formation inside the electrolytes are very important to extend the lifespan of all-solid-state lithium-metal batteries. Here, we propose a low-temperature solution-precipitation process to prepare polymer-solid electrolyte composites for a highly uniform polymer distribution in the electrolyte to enhance their mechanical strength and reduce their electronic conduction. The composites with up to 12 wt % of polymer are prepared, and the composites exhibit high ionic conductivities of up to 0.3 mS/cm. Furthermore, the electrochemical stability of the electrolyte composites on Li striping/plating cycles is investigated. We confirm that the proposed solution-precipitation process makes the composite much more stable than the bare solid electrolyte and causes them to outperform similar composites from the other existing preparation methods, such as mechanical mixing and solution dispersion.

Multifunctional binders hold great promise in advanced electrode designs for both fundamental research and practical utilization of lithium-ion batteries (LIBs). The reactions between Si/SiOx-dominated anodes with lithium are expected to be exothermic in principle, while the thermal tolerance along with the volume change makes high-temperature binders attractive for large scale roll-to-roll manufacturing. For instance, if a high temperature binder is also water soluble, it can be compatible with the current graphite-based anode manufacturing process. In this work, we present a water-soluble poly(amic acid)-based binder, which can withstand high temperature for industrial pre-lithiation process and effectively hold active materials together during repeated charge and discharge cycles. This lithium substituted poly(amic acid) binder (denoted as Li-Pa) can serve as a drop-in replacement for environmentally friendly electrode fabrication in large scale by providing aqueous solubility, exceptional thermal stability and mechanical flexibility.

Local chemical ordering (LCO) in the CrCoNi medium-entropy alloy was investigated by transmission electron microscopy (TEM) after different annealing treatments and their corresponding mechanical properties by bulk tensile tests and nanoindentation. A cold-rolled alloy was annealed at 1000°C for 0.5 h followed by ice water quenching and then aged at a number of different temperatures (600°C, 700°C, 800°C, 900°C, and 1000°C) under vacuum for 240 h to generate different degrees of chemical ordering. A splat-quenched sample rapidly cooled from the liquid phase was also examined. While bulk mechanical properties did not vary among samples with equivalent grain sizes, nanoindentation tests revealed notable differences. As indicated by the load at first pop-in using a Berkovich tip or the indentation yield strength via continuous stiffness measurements using a 10 μm spherical tip, the nanoindentation tests revealed that the stress for onset of plasticity during indentation varied with heat treatment and peaked in the 900°C aged sample. Energy-filtered TEM characterization indicated the presence of ordering in all specimens, with a higher degree of LCO in the aged samples relative to the splat-quenched and 1000°C-quenched samples. The evolution of LCO during aging was determined to occur on the time scale similar to those of bulk diffusion. The difference in nanoindentation strength was attributed to the difference in dislocation nucleation barriers imposed by different degrees of LCO.