UC Irvine

As research and industrial interest in anion-exchange membrane water electrolysis (AEMWE) grows, there is an increasing need for reliable baselines and cross-lab validation of results. The wide variety of material sets and operating conditions under consideration for AEMWE has thus far limited efforts for standardization. In this study, round-robin testing was conducted in deionized water and KOH-based supporting electrolyte by 5 institutions from academia, national laboratories, and industry to provide baseline performance data and identify sources of cross-lab variability. Baseline membrane electrode assemblies were fabricated with commercial catalysts, membranes, and transport layers using standard techniques and tested using reagent-grade electrolytes, aiming for accessibility rather than state-of-the-art performance. From all tests, the average voltage at 1 A/cm2 was 2.72 ± 0.17 V and 1.87 ± 0.03 V in deionized water and 0.1 M KOH, respectively. The maximum in-house and cross-lab variations at this current density were 118 mV and 476 mV in water and 60 and 88 mV in 0.1 M KOH. The KOH purity, station contamination, and temperature control were identified as possible factors affecting performance between labs, with in-house specific variation attributed to sample-to-sample differences in fabrication, cell assembly, and station contamination. This work provides a commercial baseline for the field and highlights the need for improved standardization and reproducibility in AEMWE research.