Lawrence Berkeley National Laboratory

A round bobbin test has been widely used to measure critical current Ic of practical superconductors including Nb–Ti, Nb3Sn, and Bi-2212 round strands at 4.2 K and in high magnetic fields but rarely used for rare earth-barium-copper-oxide (REBCO) coated conductor tapes. Here, we applies this method to REBCO tapes and test their Ic at 77 K, self-field, and 4.2 K with a magnetic field of 14 T applied parallel to the tape. The sample carries very high current densities; it is 1.3 m long and has a dense array of voltage taps that allows probing localized thermal runaways and correlation with Ic variations along the length. At 77 K, the Ic values of all sections were measured and found to be rather uniform. However, at 4.2 K, we found that a 3 cm section has 90% of the overall voltage drop and it went into thermal runaways upon further increasing current. Thus, at 4.2 K, we were prevented by localized thermal runaways and unable to determine Ic of most of the REBCO conductor sections; this behavior is different from Bi-2212 and Bi-2223 for which Ic of all turns of a round barrel sample can be determined. We simulate REBCO tapes during current ramping to a thermal runaway and analyze impacts of various factors including cooling, conductor n-values, and thickness of stabilizer on the thermal runaway current Iq. The combined experiments and simulations identify n-value as a crucial factor that leads to the observed differences between Bi-2212 and REBCO. Together with cooling and the standard deviation of Ic variations along the length, the n-value determines whether Iq is above or below the average Ic of a long piece of conductor and their ratio Iq/Ic,ave, greatly affecting quench detection and thermal runaway prevention strategies of Bi-2212 and REBCO magnets.