Lawrence Berkeley National Laboratory

This paper presents experimental results from conduction-cooled thermal testing of a ReBCO canted cosine theta (CCT) magnet (C2), originally designed and fabricated at LBNL using CORC cables. While the performance of the coil under liquid helium and nitrogen environments has been previously established, this study explores its behavior under conduction cooling using a large test cryostat at The Ohio State University. The magnet, measuring 613 mm in length and weighing 75 kg, consists of four helical layers wound with ReBCO-based CORC wire and was thermally anchored to a copper cold ring supported by a G-10 strongback. Cooling was provided by two Sumitomo RDK-415D cryocoolers, offering a combined 3 W at 4.2 K and 150 W at 77 K. Multiple thermal cycles were performed, with cooldown durations of up to 45 hours. Final base temperatures of approximately 10.8 K (at the coil edge) and 12.0 K (at the coil center) were achieved, with an axial temperature difference of approximately 1.2 K. The warm-up period extended over approximately 24.6 hours. Voltage measurements from all four layers were recorded during cooldown and warmup. The system demonstrated stable cooldown performance, repeatable gradients, and good thermal anchoring. These results support the feasibility of conduction cooling in large-scale HTS magnets, aligning with broader goals for green cryogen-free accelerator technologies and paving the way for more sustainable, scalable, and energy-efficient high-field magnet systems in next-generation particle accelerators.