Mullite/Mo interfaces formed by Intrusion bonding
The microstructure and strength of Mo/mullite interfaces formed by diffusion bonding at 1650oC has been analyzed. Interfacial metal-ceramic interlocking contributes to flexural strength of approx. 140 MPa as measured by 3 point bending. Saturation of mullite with MoO2 does not affect the interfacial strength.